32NK - эп475-VI ribbon, round, alloy

32NK - эп475-VI ribbon, round, alloy


Precision alloy 32NK-VI with specified temperature coefficient of linear expansion is used for connection with the glass and for parts with polished surface. Temperature coefficient of linear expansion ТКРх106 in the temperature range -60+20°C +20 to +100°C is not more than 1.5 [1/°C]. This alloy demonstrates a rare physical characteristics: magnetic, elastic, thermal, electrical. Belongs to the category of high-alloyed alloys. Its high quality due to the precision of the chemical. composition, thoroughness manufacturing and processing, absence of impurities. Precision alloy based on iron, Nickel, copper, niobium, cobalt, are used in precision machine tools, innovative technology and laser technology for manufacturing precision electronic devices, home appliances, calibration and instrumentation. Alloy 32NK-VI is relevant for parts with polished surface and for airtight connection with the glass.

The chemical composition of the alloy 32NK-VI, in percent.

Mn Si C Ni Cr P S Co
to 0.4 to 0.3 to 0.03 31.5 — 33 to 0.1 to 0.015 to 0.015 3.7 — 4.7
Mechanical characteristics:
 — Short-term tensile strength in [MPa] blower SB
 — Yield strength (limit of proportionality) for the residual strain, [MPa] sT
 — at break elongation in [ % ] d5
 — narrowing of the relative in [ % ] y
 — the viscosity of the shock, in [ kJ / m2] KCU
 — Brinell hardness [MPa] HB
Physical characteristics of this brand of alloy:
— 1st kind of modulus of elasticity, [MPa]  — E
— The temperature required to obtain these properties, [Grad]  — T
— linear coefficient. temp. extensions to [1/Deg] (temp. the interval 20o), -a
— electrical resistivity, [Ohm·m] -R
— The density of this material, [kg/m3] -r
— The heat capacity of the material (or conductivity) [W/(m·deg)] -l
— Specific heat of material [j/(kg·deg)] (temp. the interval 20 ° C) -C

Magnetic characteristics:

the coercive force (not more than) [A/m ] Hc
the magnetic permeability (not above) [ MH/m ] Umax
— specific losses (no higher) frequency 50 Hz, magnetic induction of 1.0 T [ W/kg ] P1.0/50
— T magnetic induction intensity of a magnetic field of not less than 100, in a magnetic field [ A/m ] B100


weldability limited

— welding is possible in the process of heating up to temp. 100−120? C and further thermal treatment


in order to obtain quality welded joints, it is necessary to perform additional operations: during welding heating up to temp. 200−300°C, heat treatment (annealing) after welding.

Welded without any restrictions

— welding is carried out without further heat treatment and pre-heating.

Buy at best price

The range of products from alloy 32NK-VI presented by LLC «AVEK global» can satisfy almost any consumer. This alloy belongs to the popular group of steel products due to its real value and variety of output options. Quality metal products is guaranteed absolute observance of all technological norms of production. In the absence of the base performance required of the product and if necessary other option products, we can produce custom sizes to order.