2.0921 - CuAl8 - C61000 pipe, wire

2.0921 - CuAl8 - C61000 pipe, wire

Supplier — AvekGlob Company — offers at a reasonable price from the manufacturer a pipe and wire made of aluminum bronze grade CuAl8 (alloy C61000, alloy 2.0921). The supplier guarantees the timely delivery of products to any address specified by the consumer.

Technical specifications

Aluminum bronze grade CuAl8 (other names — alloy C61000, alloy 2.0921) is used mainly in welding technologies, as it is ideal for welding pure and austenitic steel sheet. It maintains a good rate of welding and creates a seamless welding line. effective for butt welding of copper with steel, for engineering products and shipbuilding industry. Suitable for use in pulsed argon-arc welding, which is recommended for multi-layer hard facing of steel products.

Urgency of application

Aluminum bronze grade CuAl8 (alloy C61000, alloy 2.0921) is used in the manufacture of housing parts of plain bearings operating under abrasive and corrosive wear at a load of up to 125 MPa. Sufficient wear resistance of such products is preserved when they are used in salt water, soluble salts of various metals and many commonly used acids at different concentrations and temperatures.

Typical applications are pipe and sheet products, valve seats, etching hooks, impellers in chemical engineering and pulp and paper industry.

Chemical composition

It is given in the table:

Standard Name Make Cu Al Fe Mn Ni P Pb Si Sn Zn Other
GB / T9460 SCu6100A CuAl8 the basis 7.0−9.0 No more
0.5
No more
0.5
No more
0.5
- No more
0.02
No more
0.2
Not more than0.1

No more

0.2

No more
0.2
BS EN14640 Cu6100 CuAl8 the basis 6.0−9.5 0.5 0.5 0.8 - 0.02 0.2 - 0.2 0.4

Physical and mechanical properties

  • Density, kg / m 3 — 7700;
  • Melting point, 0 С — 1040;
  • Modulus of elasticity, GPa — 230;
  • Impact strength, kJ / m 2 — 65… 90;
  • Limit of time resistance, MPa — 450;

Yield strength, MPa — 270;

  • Relative elongation at tension,% — 40… 45;
  • Hardness in Brinell, HB, not more than — 121.

Assortment and application features

Wire made of bronze of the brand CuAl8 (alloy C61000, alloy 2.0921) for use as an electrode is manufactured in the range of diameters from 0.8 to 6. 4 mm, tubular rolling — up to 300 mm in diameter. Weldability of aluminum bronzes is good.

Supplier — AvekGlob Company — offers to buy a pipe and wire made of aluminum bronze grade CuAl8 (alloy C61000, alloy 2.0921) in a large range of sizes and lengths. Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.