2.0375 - CuZn36Pb3 - C36000 sheet, strip
Supplier — AvekGlob company — offers sheet and tape, which are made of brass CuZn36Pb3 (2.0375, C36000) at reasonable prices from the manufacturer. The supplier guarantees the timely delivery of products to any address specified by the consumer.
Copper-zinc alloy of the brand CuZn36Pb3 (other names — 2.0375, C36000) contains an increased percentage of lead, which improves the mechanical machinability of the material, its corrosion resistance, and also contributes to a significant reduction in the coefficient of friction. The latter is used in the production of high-loaded sliding bearings. However, the increased lead content leads to an increase in the degree of toxicity of the alloy, so its use in the food and pharmaceutical industry, as well as for the purposes of drinking water supply is not recommended. In the composition of the brass in question, lead forms a separate phase, so the CuZn36Pb3 (2.0375, C36000) alloy is a single-phase brass.
Urgency of application
The main applications are large sliding bearings made from cast billets and operating under conditions of elevated temperatures and specific loads.
In accordance with the technical requirements of DIN EN 17660, this alloy contains:
Copper — up to 61%;
Lead up to 3%;
Zinc is the rest.
Physical and mechanical properties
- density, kg / m 3 — 8500;
- melting point, 0 С — 885… 900;
- coefficient of thermal expansion in the temperature range 20… 200 0 С, μm / deg — 20,6;
- coefficient of thermal conductivity at room temperature, W / Mgrade — 100;
- hardness according to Brinell, НВ — 100… 140;
- limit of temporary resistance, MPa — 340… 480 (respectively, for soft and hard brass);
- yield strength, MPa — 200… 260 (respectively, for soft and hard brass);
- modulus of elasticity, GPa — 102;
- permissible tensile elongation,% — 20… 3 (respectively, for soft and hard brass).
Assortment and application features
The sheet and tape of brass CuZn36Pb3 (2.0375, C36000) are produced in a wide range of sizes, and thickness. When used, especially in ammonia-containing media in the presence of mechanical stress, there is the problem of stress corrosion cracking of the alloy. It is not recommended to use this brass in warm acid waters. Plastic molding in the cold state is limited, the temperature range of forging is 700… 800 0 С. The ability to solder and weld is average, the use of gas welding technologies is not recommended. Mechanical machinability is high, but the alloy’s grindability is poor because of the intense clogging of the surface of grinding wheels with particles of the material being processed.
Supplier — AvekGlob Company — offers to buy sheet and brass tape of CuZn36Pb3 (2.0375, C36000) in a wide assortment of cross-sectional dimensions and thickness. Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.