2.0932 - CuAl8Fe3 - C61400 sheet, strip, pipe
Supplier — AvekGlob company — offers at a reasonable price from the manufacturer a sheet of ribbon, a pipe that are made of aluminum bronze grade CuAl8Fe3 (alloy C61400, alloy 2.0932). The supplier guarantees the timely delivery of products to any address specified by the consumer.
Aluminum bronze grade CuAl8Fe3 (other names — alloy C61400, alloy 2.0932) is additionally alloyed with nickel and iron, which provides a unique combination of characteristics of medium strength, high ductility, excellent corrosion resistance in salt water. In particular, the considered brand of aluminum bronze has a higher plasticity than nickel aluminum bronzes, and can be subjected to cold treatment to significantly improve the mechanical properties. Bronze CuAl8Fe3 (alloy C61400, alloy 2.0932) retains its properties at low temperatures to -269 ºC.
After forging, the material acquires a thin, equiaxial grain structure, which guarantees the anisotropy of the properties of the products made from this bronze.
Urgency of application
Aluminum bronze grade CuAl8Fe3 (alloy C61400, alloy 2.0932) is used in many commercial and protective (marine) applications. It produces tubular plates for condensers, evaporators and heat exchangers, cryogenic equipment, water tanks, tanks for storage and operation. In engineering, this alloy is used for the production of fastening products and components of pumping units.
It is given in the table:
|Content,%||the basis||6.0−8.0||1.5−3.5||Not more than 1.0||Not more than 0.2||Not more than 0.01||Not more than 0.015|
Physical and mechanical properties
- Density, kg / m 3 — 7800;
- Melting point, 0 С — 1045… 1110;
- Modulus of elasticity, GPa — 120;
- Coefficient of thermal conductivity at room temperature, W / mgrad — 59… 71;
- Specific heat capacity, J / kggrad — 419;
- Coefficient of thermal expansion, μm / deg — 17;
- Limit of time resistance, MPa — 450… 610 (lower values for annealed material);
Yield strength, MPa — 195… 390 (lower values for annealed material);
- Relative elongation at tension,% — 35… 90 (lower values — for cold-worked material);
- Hardness in Brinell, HB, not more than — 121.
Assortment and application features
Rolled bronze CuAl8Fe3 (alloy C61400, alloy 2.0932) is made from 0.8 to 4.0 mm thick, with a width of up to 2000 mm (sheet) and up to 400 mm — a tape (the maximum pipe diameter is 400 mm… 925 0 С. The maximum temperature of operation of products made from this alloy is 300 ° C.
Supplier — the company AvekGlob — offers to purchase a sheet, tape, pipe, made of aluminum bronze grade CuAl8Fe3 (alloy C61400, alloy 2.0932). Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.