Brof 6.5-0.15 tape, strip
.jpg)
Industrial use: for bushings, springs and bearings
Brof6.5−0.15 — belongs to the class of tin bronze, processed under pressure.
Characteristics of tin bronzes
Bronze tin have elevated anti-friction quality, they are non-magnetic, cold-resistant, insensitive to overheating, have low volume shrinkage (about 0.8%), so widely used in art casting. The main disadvantage of tin bronzes is the formation of small pores in castings that may result in reduction tightness. Bronze tin lagerbuchse lead, zinc, Nickel, phosphorus.
Vyplavke
In the smelting process of copper and tin is formed solid solutions strongly prone to phase separation due to the high temperature interval of crystallization. Containing tin alloys over 5% have in its structure due to segregation eutectoid component e (a+d), which consists of hard and soft phases.
Basic quality
The structure of this alloy is for parts favorable sliding bearings: solid particles provide abrasion resistance, the soft phase gives excellent pererabatyvaemogo, therefore, tin bronze are excellent antifriction materials.
The coefficient of friction with lubrication is 0.01
The coefficient of friction without lubrication is 0.12
Hardness of alloy: HB 10-1 = 70 — 90 MPa
Melting point: 995°C
The percentage composition of the alloy Brof6.5−0.15
| Cu | 92,65 — 93,9 |
|---|---|
| Al | to 0.002 |
| Si | to 0.002 |
| Fe | to 0.05 |
| P | 0,1 — 0,25 |
| Sn | 6 — 7 |
| Bi | to 0.002 |
| Sb | to 0.002 |
| Mechanical characteristics Brof6.5−0.15 at a temperature of 20°C | |||||||
|---|---|---|---|---|---|---|---|
| Rental | σв (MPa) | sT (MPa) | KCU (kJ / m2) | δ5 (%) | Eg. | Size | ψ % |
| soft alloy | 300−450 | 60−70 | |||||
| hard alloy | 700−800 | 7−10 | |||||
| Physical characteristics grade alloy Brof6.5−0.15 | ||||||
|---|---|---|---|---|---|---|
| a 10-6(1/Deg) | 10 E— 5(MPa) | T (Deg) | l (W/(m·deg)) | 10 R9(Ω·m) | C (j/(kg·hail)) | r (kg/m3) |
| 1.12 | 20 | 71.4 | 160 | 8800 | ||
| 17.1 | 100 | |||||
| Designations: | ||||
|---|---|---|---|---|
| is the relative draught in processe the appearance of the first cracks, in % | å | — the ultimate tensile strength (rupture strength), MPa | σв | |
| — maximum shear stress, the ultimate strength in torsion, MPa | Jê | — the limit of elasticity in MPa | σ0,05 | |
| — tensile strength during bending in MPa | σизг | — yield strength, MPa | σ0,2 | |
| — the endurance limit during the test with a symmetrical cycle of loading in bending, MPa | σ-1 | — relative elongation after rupture, % | δ5,δ4,δ10 | |
| — the endurance limit during testing with a symmetrical load cycle torsion, MPa | J-1 | — yield strength (compression), in MPa | σсж0,05 and σсж | |
| — number of loading cycles | n | — the relative shift in % | ν | |
| — specific email. resistance, Ohm·m | R and ρ | — short-term tensile strength, in MPa | blower SB | |
| is the normal modulus of elasticity, GPA | E | contraction ratio in % | ψ | |
| temperature get the properties, Grad | T | — impact strength installed in the specimens with concentrators in accordance with the type of V and U, in j/cm2 | KCU and KCV | |
| — the heat capacity of the alloy (coefficient of thermal conductivity) in W/(m·°C) | l and ë | — residual deformation — the yield strength (limit of proportionality), in MPa | sT | |
| — specific heat of the alloy (temperature range 20o), in [j/(kg·deg)] | C | — Brinell hardness number | HB | |
| — density in kg/m3 | pn and r | — hardness according to Vickers | HV | |
| — coefficient of linear thermal expansion (in the temperature range 20o), 1/°C | and | — Rockwell hardness, SHK. With | HRC | |
| — long-term strength, MPa | σtТ | — Rockwell hardness, SHK. In | HRB | |
| — the modulus of elasticity is in the process of shear in torsion, HPa | G | — hardness shore | HSD | |
Buy at best price
Rental, manufactured by LLC «AVEK global» bronze brand Brof6.5−0.15 will satisfy any demands. Popular products from this alloy is due to excellent quality products, a wide variety of options and the actual cost. All the products from bronze alloys produced by our company, is produced under the complete technological control at all stages that guarantees the highest quality products. The company «AVEK global» is ready to manufacture custom products non-standard sizes. Manufacturing process capabilities allow us to execute orders according to individual drawings in the absence of the required type of product in standard version.