Brkh - CuCr sheet, strip, pipe
The use of bronze alloy Brkh
Industrial use: electric parts, electrodes for welding equipment and welding machines.
Class: bronze without tin pressure treated
| Chemical composition of alloy grades Brkh | |
|---|---|
| Cr | 0,4 — 1,2 |
| Cu | 98,5 — 99,6 |
| The mechanical characteristics of the brand Brkh at 20°C | |||||||
|---|---|---|---|---|---|---|---|
| Rental | δ5 (%) | sT (MPa) | KCU (kJ / m2) | σв (MPa) | Eg. | Size | ψ % |
| soft alloy | 60−70 | 300−450 | |||||
| hard alloy | 7−10 | 700−800 | |||||
| Physical characteristics grade alloy Brkh | ||||||
|---|---|---|---|---|---|---|
| 10 R9(Ω·m) | C (j/(kg·hail)) | r (kg/m3) | l (W/(m·deg)) | a 10-6(1/Deg) | E 10-5(MPa) | T (Deg) |
| 8900 | 17 | 1.12 | 20 | |||
The basic qualities
Bronze without tin in its composition does not contain scarce tin. They can be substitutes for tin bronzes, as their mechanical, corrosion and technological properties of bronze without tin, they are often superior. Without tin bronze can be not only beryllium but of the manganese, aluminum, depending on the main alloying component. Bronze beryllium are produced in accordance with GOST 18175−78. This standard applies to bronze without tin, which are processed under pressure and designed for the production of semi-finished products.
The coefficient of friction with lubrication is 0.01
The coefficient of friction without lubrication = 0.12
Hardness of alloy: HB 10-1 = 70 — 90 MPa
Melting point: 995°C
| Designations: | ||||
|---|---|---|---|---|
| is the relative draught in processe the appearance of the first cracks, in % | å | — the ultimate tensile strength (rupture strength), MPa | σв | |
| — maximum shear stress, the ultimate strength in torsion, MPa | Jê | — the limit of elasticity in MPa | σ0,05 | |
| — tensile strength during bending in MPa | σизг | — yield strength, MPa | σ0,2 | |
| — the endurance limit during the test with a symmetrical cycle of loading in bending, MPa | σ-1 | — relative elongation after rupture, % | δ5,δ4,δ10 | |
| — the endurance limit during testing with a symmetrical load cycle torsion, MPa | J-1 | — yield strength (compression), in MPa | σсж0,05 and σсж | |
| — number of loading cycles | n | — the relative shift in % | ν | |
| — specific email. resistance, Ohm·m | R and ρ | — short-term tensile strength, in MPa | blower SB | |
| is the normal modulus of elasticity, GPA | E | contraction ratio in % | ψ | |
| temperature get the properties, Grad | T | — impact strength installed in the specimens with concentrators in accordance with the type of V and U, in j/cm2 | KCU and KCV | |
| — the heat capacity of the alloy (coefficient of thermal conductivity) in W/(m·°C) | l and ë | — residual deformation — the yield strength (limit of proportionality), in MPa | sT | |
| — specific heat of the alloy (temperature range 20°C), in [j/(kg·deg)] | C | — Brinell hardness number | HB | |
| — density in kg/m3 | pn and r | — hardness according to Vickers | HV | |
| — coefficient of linear thermal expansion (in the temperature range of 20°C), in 1/°C | and | — Rockwell hardness, SHK. With | HRC | |
| — long-term strength, MPa | σtТ | — Rockwell hardness, SHK. In | HRB | |
| — the modulus of elasticity is in the process of shear in torsion, HPa | G | — hardness shore | HSD | |
Buy at best price
The company LLC «AVEK global» bronze brand Brkh will satisfy any demands. Popular products from this alloy is due to excellent quality products, a wide variety of options and the actual cost. All the products from bronze alloys produced by our company, is produced under the complete technological control at all stages that guarantees the highest quality products. The company «AVEK global» is ready to manufacture custom products non-standard sizes. Manufacturing process capabilities allow us to execute orders according to individual drawings in the absence of the required type of product in standard version.