18KHG - 16MnCr5 - 16hg round, rod, forging

18KHG - 16MnCr5 - 16hg round, rod, forging

Supplier — AvecGlob Company — offers at a reasonable price from the manufacturer a circle, bars, which are made of steel grade 18HG (16MnCr5, 16hg). The supplier guarantees the timely delivery of products to any address specified by the consumer.

Technical specifications

Low-carbon steel grade 18ХГ (the nearest foreign analogues — steel 16MnСr5, 16hg) is a structural steel alloyed with chromium and silicon. Abroad is also produced according to the AISI 1.7131 standard. It is well amenable to chemical-thermal treatment, as a result of which it significantly increases the surface hardness and wear resistance in the sliding nodes. The presence of chromium increases the heat resistance of the material, but the combined effect of chromium, manganese and silicon limits plasticity at room temperatures. Has good resistance to operation in non-aggressive environments.

Urgency of application

Due to increased wear resistance, 18ХГ steel (16MnСr5, 16hg) is used in the manufacture of piston bolts, rods, camshafts, oil distillers, levers and other similar products in the automotive, pipeline and general engineering industries.

Chemical composition

According to the technical requirements of the standard GOST 4543−91, the following elements are included in steel 18ХГ steel (numerical data — in percentage):

C Si Mn Ni S P Cr Cu
0.15 — 0.21 0.17 — 0.37 0.9 — 1.2 up to 0,3 up to 0.035 up to 0.035 0.9 — 1.2 up to 0.3

Physical and mechanical properties

  • density, kg / m 3 — 7800;
  • melting point, 0 C -1490;
  • coefficient of thermal expansion in the temperature range 20… 100 0 С, μm / deg — 10,5;
  • Specific heat, J / ggrad — 510;
  • modulus of elasticity, GPa — 210;
  • coefficient of thermal conductivity in the temperature range 20… 100 0 С, W / mgrad — 37;
  • hardness according to Brinell, HB — 187;
  • limit of time resistance, MPa — 880;
  • yield strength, MPa-635;
  • Relative narrowing of the cross-sectional area. % — 40;
  • permissible tensile elongation,% — 10.

Assortment and application features

The circle and rod of low-alloy structural steel 18ХГ (16MnСr5, 16hg) are produced in a wide range of cross-sections and length. Mechanical machinability and weldability are average. The material is sensitive to flocculation and to temper brittleness. The temperature range of forging is 830… 1220 0 С.

Supplier — AvekGlob Company — offers to buy a rod or a circle of low-carbon structural steel 18ХГ (16MnСr5, 16hg) in the required assortment of cross sections and length. Products can be bought at a price formed on the basis of European and world standards of production. Implementation is possible in bulk and retail, for regular customers, a flexible system of discounts operates.